Gloss Lubricant TAS-2A

Gloss Lubricant TAS-2A Specifications: White or slightly yellow powder, Melting temperature: 65 Colour: ≤5.0(Gardner) Flash Point: ≥275 Acid content: ≤10.0 KOH mg/g Heat Weight Loss : ≤1.8wt%(250), ≤4.8wt%(300) Characterizations: TAS-2A is amide based high efficient gloss lubrication dispersant.It is insoluble in water, ethanol, acetone, carbon tetrachloride solvents at room temperature, but soluble in hot halogenated hydrocarbons, resists to acid and base, and nontoxic. It owns the following characters: 1, improve the dispersibility of pigments or fillers; 2, enhance MFR and surface gloss of the composites; 3, reduce the screw torque , so decrease machinery wear and tear; 4, improve the mechanical properties of the composites. Applications: It is mainly used in the general thermoplastics composites such as PE, PP, PVC ABS and their masterbatch. Recommendation content 3 5wt% (PE, PP and PVC masterbatch); 5 8wt%( ABS masterbatch). In constrat with EBS, WAX(BASF Corporation.), PE520(Clariant Corporation), if there are the same gloss and dispersion in the composites modified by TAS-2A, the content of modifier (TAS-2A) can be reduced 30-40%. Some examples for TAS-2A application are given in the following tables. Table 1 Name Main Components PHRTAS-2A (PHRMelt IndexPP Retardant Masterbatch10 PBBs ether 50-605-618.0g/10min( 190°C, 2.16kg)ABS white MasterbatchTiO2 605-813.5g/10min( 200°C, 5kg)ABS grey MasterbatchPigment 605-823.5g/10min( 200°C, 5kg) Table 2 1#2#3#4#FormulaPP(PHR)100100100100Inorganic FillerPHR40(filler A)40(filler A)40(filler B)40(filler B)Coupling Agent PHR0.40.40.4TAS-2A(PHR)0.50.5PropertiesGlossGS60°62.772.8831.232.2Impact Strength (J/m)243.5270.9Flexural Modulus, (Mpa)28323332Tensile Strength,Mpa13.214.3MFR(g/10min) 18.325.7 Storage: Keep away from moisture and fire source. Packing: PE woven bag combined with kraft paper 25kg/bag.